Título: Corrosion behavior of UNS S31803 steel with changes in the volume fraction of ferrite and the presence of chromium nitride.
Autor(es): Lacerda, José Carlos de
Cândido, Luiz Cláudio
Godefroid, Leonardo Barbosa
Palavras-chave: Stainless steel
Polarization
Pitting corrosion
Stress corrosion cracking
Data do documento: 2015
Referência: LACERDA, J. C. de; CÂNDIDO, L. C.; GODEFROID, L. B. Corrosion behavior of UNS S31803 steel with changes in the volume fraction of ferrite and the presence of chromium nitride. Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing, p. 428-435, 2015. Disponível em: <http://www.sciencedirect.com/science/article/pii/S0921509315304305>. Acesso em: 11 jul. 2016.
Resumo: The goal of this study was to examine the changes caused in stress corrosion cracking and the critical pitting temperature behavior of a UNSS31803 duplex stain less steel due to variations in the ferrite fraction and the presence of chromium nitride in their microstructure. The steel plates were cold rolled and annealed at 1060 °C. Microstructural variations in the plates were produced by thermal annealing treatments a t1200 °C and 1300 °C. Steel annealed at 1060 °C showed greater resistance to stress corrosion cracking than steel annealed at 1300 °C. Steel annealed at 1300 °C had the lowest critical pitting temperature.
URI: http://www.repositorio.ufop.br/handle/123456789/6769
DOI: https://doi.org/10.1016/j.msea.2015.09.092
ISSN: 0921-5093
Licença: O periódico Materials Science and Engineering: A concede permissão para depósito deste artigo no Repositório Institucional da UFOP. Número da licença: 3914191502183.
Aparece nas coleções:DEMET - Artigos publicados em periódicos

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
ARTIGO_CorrosionBehaviorUNS.pdf3,03 MBAdobe PDFVisualizar/Abrir


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.