Title: | Effect of volume fraction of phases and precipitates on the mechanical behavior of UNS S31803 duplex stainless steel. |
Authors: | Lacerda, José Carlos de Cândido, Luiz Cláudio Godefroid, Leonardo Barbosa |
Keywords: | Duplex stainless steel Microstructure Tensile and fatigue tests |
Issue Date: | 2015 |
Citation: | LACERDA, J. C. de; CÂNDIDO, L. C.; GODEFROID, L. B. Effect of volume fraction of phases and precipitates on the mechanical behavior of UNS S31803 duplex stainless steel. International Journal of Fatigue, v. 74, p. 38, 2015. Disponível em: <http://www.sciencedirect.com/science/article/pii/S0142112314003260>. Acesso em: 09 abr. 2015. |
Abstract: | Mechanical properties of a grade UNS S31803 duplex stainless steel were studied. Samples were annealed at three different temperatures, 1060 C, 1200 C, and 1300 C, to change the a/c proportion, to precipitate undesirable phases (for example, a0 , r and chromium nitrides), and to study the effect of the microstructure on the mechanical behavior. Specimens with a thickness of 1.8 mm were prepared according to ASTM standards and tested at room temperature. Tensile tests were conducted using displacement control at a rate of 5 mm/min. Force-controlled constant amplitude axial fatigue tests were conducted at a frequency of 30 Hz and an R stress ratio of 0.1. Microstructural analyses, performed by optical microscopy and scanning electron microscopy, showed the following modifications to the microstructure: changes in the phase volume fractions, the phase grain growths, and the morphology of the c-phase and the precipitation of chromium nitrides in the a-phase. The mechanical properties of the steel were significantly changed due to the changed microstructure. The results demonstrate the sensitivity of the steel to the annealing temperature. |
URI: | http://www.repositorio.ufop.br/handle/123456789/5347 |
metadata.dc.identifier.doi: | https://doi.org/10.1016/j.ijfatigue.2014.12.015 |
ISSN: | 0142-1123 |
metadata.dc.rights.license: | O periódico International Journal of Fatigue concede permissão para depósito deste artigo no Repositório Institucional da UFOP. Número da licença: 3624211041567. |
Appears in Collections: | DEMET - Artigos publicados em periódicos |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
ARTIGO_EffectVolumeFraction.pdf | 3,28 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.