Título : | Synchrotron X-ray diffraction and Raman spectroscopy of Ln3NbO7 (Ln=La, Pr, Nd, Sm-Lu) ceramics obtained by molten-salt synthesis. |
Autor : | Siqueira, Kisla Prislen Félix Soares, J. C. Granado, Eduardo Bittar, Eduardo Matzenbacher Paula, Ana Maria de Moreira, Roberto Luiz Dias, Anderson |
Palabras clave : | Synchrotron X-ray diffraction Rare earth Niobates Raman spectroscopy |
Fecha de publicación : | 2014 |
Citación : | SIQUEIRA, K. P. F. et al. Synchrotron X-ray diffraction and Raman spectroscopy of Ln3NbO7 (Ln=La, Pr, Nd, Sm-Lu) ceramics obtained by molten-salt synthesis. Journal of Solid State Chemistry, v. 209, p. 63-68, 2014. Disponível em: <http://www.sciencedirect.com/science/article/pii/S0022459613004726>. Acesso em: 02 fev. 2015. |
Resumen : | Ln3NbO7 (Ln=La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu) ceramics were obtained by molten- salt synthesis and their structures were systematically investigated by synchrotron X-ray diffraction (SXRD), second harmonic generation (SHG) and Raman spectroscopy. It was observed that ceramics with the largest ionic radii (La, Pr, Nd) crystallized in to the Pmcn space group, while the ceramics with intermediate ionic radii (Sm-Gd) exhibited different crystal structure belonging to the Ccmm space group. For this last group of ceramics, this result was corroborated by SHG and Raman scattering and ruled out any possibility for the non-centrosymmetric C 2221 space group, solving a recent controversy in the literature. Finally, according to SXRD, Tb-Lu containing samples exhibited an average defect fluorite structure (Fm3m space group). Nonetheless, broad scatter in gat forbidden Bragg reflections indicates the presence of short-range domains with lower symmetry. Vibrational spectroscopy showed the presence of six Raman-active modes, inconsistent with the average cubic fluorite structure, and in line with the existence of lower-symmetry nano-domains immersed in the average fluorite structure of these ceramics. |
URI : | http://www.repositorio.ufop.br/handle/123456789/4888 |
metadata.dc.identifier.doi: | https://doi.org/10.1016/j.jssc.2013.10.015 |
ISSN : | 0022-4596 |
metadata.dc.rights.license: | O periódico Journal of Solid State Chemistry concede permissão para depósito deste artigo no Repositório Institucional da UFOP. Número da licença: 3577170654861. |
Aparece en las colecciones: | DEQUI - Artigos publicados em periódicos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
ARTIGO_SynchrotronXRay.pdf | 873,47 kB | Adobe PDF | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.