Cardoso, Afonso Vaz de MelloPaolinelli, Sebastião da CostaSilveira, Carolina CesconettoCota, André Barros2019-06-062019-06-062018CARDOSO, A. F. de M. et al. Secondary recrystallization characteristics of 3%Si grain-oriented electrical steel. Journal of Materials Research and Technology - JMR&T, v. 8, n. 1, p. 240-245, jan./mar. 2018. Disponível em: <https://www.sciencedirect.com/science/article/pii/S2238785417301990>. Acesso em: 19 mar. 2019.2238-7854http://www.repositorio.ufop.br/handle/123456789/11468A secondary recrystallization Lab study focusing on the secondary recrystallization temper- ature and magnetic properties was carried out on cold rolling industrial samples of 3%Si grain-oriented electrical steel produced by low slab reheating temperature technology. The results showed a secondary recrystallization temperature, determined by the observed grain size change, of 1080 ◦C with annealing interruption and of 1060 ◦C in annealing for 50 h at constant temperature. In addition, the best set of magnetic properties, the higher induction and the lower core loss values, was achieved by annealing the samples during 50 h at 1070 ◦C constant temperature.en-USabertoGrain-oriented steelMagnetic propertiesArtigo publicado em periodicoThis is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/). Fonte: o próprio artigo.https://doi.org/10.1016/j.jmrt.2017.12.002