Determinação da temperatura de recristalização secundária do aço elétrico de grão orientado produzido com baixa temperatura de reaquecimento de placa.
dc.contributor.advisor | Cota, André Barros | pt_BR |
dc.contributor.advisor | Paolinelli, Sebastião da Costa | pt_BR |
dc.contributor.author | Cardoso, Afonso Vaz de Mello | |
dc.contributor.referee | Cota, André Barros | pt_BR |
dc.contributor.referee | Pires, José Carlos dos Santos | pt_BR |
dc.contributor.referee | Paolinelli, Sebastião da Costa | pt_BR |
dc.contributor.referee | Silva, Gilberto Henrique Tavares Álvares da | pt_BR |
dc.date.accessioned | 2018-06-08T15:59:44Z | |
dc.date.available | 2018-06-08T15:59:44Z | |
dc.date.issued | 2017 | |
dc.description | Programa de Pós-Graduação em Engenharia de Materiais. Departamento de Engenharia Metalúrgica, Escola de Minas, Universidade Federal de Ouro Preto. | pt_BR |
dc.description.abstract | Recentes demandas do setor energético por menores desperdícios durante a geração e transmissão de energia trazem a necessidade de desenvolvimento de aços elétricos com melhores propriedades e menores custos de produção. O aço elétrico de grão orientado produzido com baixa temperatura de reaquecimento de placa é uma alternativa para sanar algumas das atuais necessidades do setor. Além de possuir melhores propriedades magnéticas, aumentando a eficiência de transformadores, este aço traz outras vantagens em relação ao aço elétrico de grão orientado convencional, como um processo de produção de menor custo. Um estudo laboratorial focado em temperaturas de recristalização secundária e propriedades magnéticas de aços elétricos de grão orientado produzido com baixa temperatura de reaquecimento de placa foi conduzido em amostras industriais laminadas a frio de aço 3%Si. Os resultados mostraram uma temperatura de recristaliação secundária de 1080°C definida por meio de ciclos de recozimento interrompidos e de 1060°C por meio de ciclos de recozimento com encharque de 50 horas em temperatura constante, definidas por meio de análise de alterações microestruturais. Também foi verificado um melhor valor de propriedades magnéticas, maior indução e menor perda magnética, nas amostras que passaram por tratamento térmico com encharque de 50 horas na temperatura de 1070°C. | pt_BR |
dc.description.abstracten | Recent demands of the energy sector bring the need for development of electrical steels with improved properties and lower production cost. The oriented grain electrical steel produced with low reheating temperature is an alternative to remedy some of the current industry needs. Besides having better magnetic properties, increasing the efficiency of transformers, the steel brings other advantages relative to conventional oriented grain electrical steel, a lower cost production process. A secondary recrystallization Lab study focusing on the secondary recrystallization temperature and magnetic properties was carried out on cold rolling industrial samples of 3%Si grain-oriented electrical steel produced by low slab reheating temperature technology. The results showed a secondary recrystallization temperature 1080°C by annealing interrupting and grain size change observation and 1060°C by annealing during 50h at constant temperature. In addition, the best set of magnetic properties, the higher induction and the lower core loss values, was achieved by annealing the samples during 50h at 1070°C constant temperature. | pt_BR |
dc.identifier.citation | CARDOSO, Afonso Vaz de Mello. Determinação da temperatura de recristalização secundária do aço elétrico de grão orientado produzido com baixa temperatura de reaquecimento de placa. 2017. 53 f. Dissertação (Mestrado em Engenharia de Materiais) – Escola de Minas, Universidade Federal de Ouro Preto, Ouro Preto, 2017. | pt_BR |
dc.identifier.uri | http://www.repositorio.ufop.br/handle/123456789/9984 | |
dc.language.iso | pt_BR | pt_BR |
dc.rights | aberto | pt_BR |
dc.rights.license | Autorização concedida ao Repositório Institucional da UFOP pelo(a) autor(a) em 23/01/2018 com as seguintes condições: disponível sob Licença Creative Commons 4.0 que permite copiar, distribuir e transmitir o trabalho desde que sejam citados o autor e o licenciante. Não permite o uso para fins comerciais nem a adaptação. | pt_BR |
dc.subject | Recristalização - metalurgia | pt_BR |
dc.subject | Grão orientado | pt_BR |
dc.subject | Metais - tratamento térmico | pt_BR |
dc.subject | Aço - propriedades elétricas | pt_BR |
dc.title | Determinação da temperatura de recristalização secundária do aço elétrico de grão orientado produzido com baixa temperatura de reaquecimento de placa. | pt_BR |
dc.type | Dissertacao | pt_BR |
Arquivos
Pacote Original
1 - 1 de 1
Nenhuma Miniatura disponível
- Nome:
- DISSERTAÇÃO_DeterminaçãoTemperaturaRecristalização.pdf
- Tamanho:
- 2.23 MB
- Formato:
- Adobe Portable Document Format
Licença do Pacote
1 - 1 de 1
Nenhuma Miniatura disponível
- Nome:
- license.txt
- Tamanho:
- 924 B
- Formato:
- Item-specific license agreed upon to submission
- Descrição: