Estudo da degradação mecânica de pequenas quantidades de coque em testes de tamboreamento.
dc.contributor.advisor | Assis, Paulo Santos | pt_BR |
dc.contributor.advisor | Silva, Guilherme Liziero Ruggio da | pt_BR |
dc.contributor.author | Silva, Antonio Marlon Barros | |
dc.contributor.referee | Assis, Paulo Santos | pt_BR |
dc.contributor.referee | Silva, Guilherme Liziero Ruggio da | pt_BR |
dc.contributor.referee | Assis, Carlos Frederico Campos de | pt_BR |
dc.contributor.referee | Murta, Carlo Luiz B. | pt_BR |
dc.date.accessioned | 2017-02-16T17:03:15Z | |
dc.date.available | 2017-02-16T17:03:15Z | |
dc.date.issued | 2016 | |
dc.description | Programa de Pós-Graduação em Engenharia de Materiais. Departamento de Engenharia Metalúrgica, Escola de Minas, Universidade Federal de Ouro Preto. | pt_BR |
dc.description.abstract | Esse estudo visa avaliar a resistência mecânica a frio do coque, utilizando pequenas quantidades (300 a 1200 g) desse material, como alternativa aos testes usuais que utilizam 10 e 50 kg de coque. Para isso, as degradações volumétrica e superficial foram avaliadas em um tambor de menores dimensões (Diâmetro: 268 mm, comprimento: 470 mm), bem como no tambor especificado pela norma JIS K2151 (1.5x1.5 m). Para o equipamento menor encontrou-se que a taxa de degradação superficial (K) aumenta ligeiramente com a massa tamboreada. O fator de maior relevância foi a velocidade de rotação do tambor, que variou de 24 a 85 rpm. Nesse caso, K decresce com a velocidade. Embora a 24 rpm a taxa de degradação superficial tenha sido alta, a quebra volumétrica não ocorreu de forma relevante, sendo que essa ocorreu somente acima de 45 rpm. No tambor maior obteve-se uma maior degradação (volumétrica e superficial), em comparação com o tambor menor. Entretanto, há uma boa correlação entre a degradação nos dois equipamentos, possibilitando obter funções para se estimar a degradação que seria obtida no tambor maior mediante a degradação observada no tambor menor, ou seja, é possível avaliar a degradação do coque utilizando pequenas quantidades desse material. | pt_BR |
dc.description.abstracten | This study aims to evaluate the coke’s cold strength using small sample mass (300 to 1200g) in alternative to the usual tests which use 10 to 50 kg of coke . For this objective the surface and volume breakage were evaluated in a small drum (268 mm in diameter and 470 mm in length) as well as in the drum specified by the regulation JIS K2151 (1.5 m in diameter and 1.5 m in length). For the small equipment it was found that the surface breakage rate constant (K) slightly increases with the mass tumbled. The most relevant factor was the drum rotation speed that varied from 24 to 85 rpm. In this case, K decreases as speed decreases too. Although at 24 rpm this surface breakage was high, the volume breakage did not occur relevantly, and this happened only above 45 rpm. When the tumbling was conducted in a bigger drum (1.5 m x 1.5 m), it was obtained a higher degradation, comparing to the smaller drum. However, there is a close relationship between the degradation in both drums, allowing to obtain functions that correlate degradation observed in the smaller drum, that is, it is possible to evaluate the coke’s degradation using small quantities of this raw material. | pt_BR |
dc.identifier.citation | SILVA, Antonio Marlon Barros. Estudo da degradação mecânica de pequenas quantidades de coque em testes de tamboreamento. 2016. 110 f. Dissertação (Mestrado em Engenharia de Materiais) – Escola de Minas, Universidade Federal de Ouro Preto, Ouro Preto, 2016. | pt_BR |
dc.identifier.uri | http://www.repositorio.ufop.br/handle/123456789/7267 | |
dc.language.iso | pt_BR | pt_BR |
dc.rights | aberto | pt_BR |
dc.rights.license | Autorização concedida ao Repositório Institucional da UFOP pelo(a) autor(a) em 14/02/2017 com as seguintes condições: disponível sob Licença Creative Commons 4.0 que permite copiar, distribuir e transmitir o trabalho desde que sejam citados o autor e o licenciante. Não permite o uso para fins comerciais nem a adaptação. | pt_BR |
dc.subject | Coque metalúrgico | pt_BR |
dc.subject | Resistência de materiais | pt_BR |
dc.subject | Teste de tamboreamento | pt_BR |
dc.subject | Confiabilidade - engenharia | pt_BR |
dc.title | Estudo da degradação mecânica de pequenas quantidades de coque em testes de tamboreamento. | pt_BR |
dc.type | Dissertacao | pt_BR |
Arquivos
Pacote Original
1 - 1 de 1
Nenhuma Miniatura disponível
- Nome:
- DISSERTAÇÃO_EstudoDegradaçãoMecânica.pdf
- Tamanho:
- 2.7 MB
- Formato:
- Adobe Portable Document Format
Licença do Pacote
1 - 1 de 1
Nenhuma Miniatura disponível
- Nome:
- license.txt
- Tamanho:
- 924 B
- Formato:
- Item-specific license agreed upon to submission
- Descrição: