Title: Desgaste de poliuretano por erosão úmida : desenvolvimento de um ensaio tecnológico.
Authors: Silva, Vinicius Augusto da
metadata.dc.contributor.advisor: Costa, Adilson Rodrigues da
Keywords: Minério de ferro
Polímeros - fratura
Desgaste mecânico
Abrasão química
Issue Date: 2017
metadata.dc.contributor.referee: Costa, Adilson Rodrigues da
Solé, Rubén Antonio Llobell
Coelho, Bruno Nazário
Moreira, Vinicius Sena
Citation: SILVA, Vinicius Augusto da. Desgaste de poliuretano por erosão úmida: desenvolvimento de um ensaio tecnológico. 2017. 71 f. Dissertação (Mestrado em Engenharia de Materiais) – Escola de Minas, Universidade Federal de Ouro Preto, Ouro Preto, 2017.
Abstract: A crescente utilização de minério de ferro e a diminuição de jazidas com minérios de teor elevado em ferro para a produção de aço têm forçado cada vez mais as mineradoras a explorarem suas reservas minerais de baixo teor de ferro. Durante o processo de tratamento e transporte destes minerais utiliza-se de tubulações que possibilitam a movimentação do minério moído e diluído em água. No entanto, o baixo teor de ferro somado aos altos teores de silicatos, altamente abrasivos, contidos nestes minerais resulta no aumento significativo do desgaste das superfícies em contato com esta polpa de minério. Diante da atual demanda de produção do minério de ferro e devido ao acentuado desgaste provocado nas tubulações e equipamentos nas etapas de tratamento e transporte de concentrado o presente trabalho objetivou avaliar o comportamento ao desgaste por erosão úmida de amostras de poliuretano utilizado para revestir as tubulações de polpa de concentrado de minério de ferro. Para esse fim foi desenvolvido um ensaio tecnológico capaz de simular as condições de desgaste por erosão úmida.
metadata.dc.description.abstracten: The increasing use of iron ore and the reduction of ore deposits with high iron content for steel production have increasingly forced mining companies to exploit their low iron ore reserves. During the process of treatment and transportation of these minerals, uses pipes that allow the movement of ore milled and diluted in water. However, the low iron content in addition to the high levels of highly abrasive silicates contained in these minerals results in a significant increase in wear on the surfaces in contact with the ore pulp. In view of the current demand for iron ore production and due to the pronounced wear as a result of the piping and the equipment in the stages of treatment and transportation of concentrate, this study had the objective to evaluate the erosion wear behavior of wet samples of polyurethane used to coat the tubes of concentrated iron ore pulp. For this purpose a technology test was developed capable of simulating wet erosion conditions.
Description: Programa de Pós-Graduação em Engenharia de Materiais. Departamento de Engenharia Metalúrgica, Escola de Minas, Universidade Federal de Ouro Preto.
URI: http://www.repositorio.ufop.br/handle/123456789/8989
metadata.dc.rights.license: Autorização concedida ao Repositório Institucional da UFOP pelo(a) autor(a) em 26/09/2017 com as seguintes condições: disponível sob Licença Creative Commons 4.0 que permite copiar, distribuir e transmitir o trabalho desde que sejam citados o autor e o licenciante. Não permite o uso para fins comerciais nem a adaptação.
Appears in Collections:REDEMAT - Mestrado (Dissertações)

Files in This Item:
File Description SizeFormat 
DISSERTAÇÃO_DesgastePoliuretanoErosão.pdf2,25 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons