Título : d-FeOOH : a superparamagnetic material for controlled heat release under AC magnetic field.
Autor : Chagas, Poliane
Silva, Adilson Cândido da
Passamani, Edson Caetano
Ardisson, José Domingos
Oliveira, Luiz Carlos Alves de
Fabris, José Domingos
Paniago, Roberto Magalhães
Monteiro, Douglas Santos
Pereira, Márcio César
Palabras clave : Iron oxides
Magnetic properties
Fecha de publicación : 2013
Citación : CHAGAS, P. et al. d-FeOOH: a superparamagnetic material for controlled heat release under AC magnetic field. Journal of Nanoparticle Research, v. 15, p. 1537-1544, 2013. Disponível em:<https://link.springer.com/article/10.1007%2Fs11051-013-1544-2>. Acesso em: 16 jun. 2017.
Resumen : Experimental evidences on its in vitro use reveal that d-FeOOH is a material that release-controlled amount of heat if placed under an AC magnetic field. d-FeOOH nanoparticles were prepared by precipitating Fe(OH)2 in alkaline solution followed by fast oxidation with H2O2. XRD and 57Fe Mo¨ssbauer spectroscopy data confirmed that d-FeOOH is indeed the only iron-bearing compound in the produced sample. TEM images evidence that the averaged particle sizes for this d-FeOOH sample is 23 nm.Magnetization measurements indicate that these d-FeOOH particles behave superparamagnetically at 300 K; its saturationmagnetization was found to be 13.2 emu g-1; the coercivity and the remnant magnetization were zero at 300 K. The specific absorption rate values at 225 kHz were 2.1, 6.2, and 34.2 W g-1, under 38, 64, and 112 mT, respectively. The release rate of heat can be directly controlled by changing the mass of d-FeOOHnanoparticles. In view of these findings, the so-preparedd-FeOOHis a real alternative tobe further tested as amaterial formedicalpractices in therapies involving magnetic hyperthermia as in clinical oncology.
URI : http://www.repositorio.ufop.br/handle/123456789/8141
metadata.dc.identifier.uri2: https://link.springer.com/article/10.1007%2Fs11051-013-1544-2
metadata.dc.identifier.doi: https://doi.org/10.1007/s11051-013-1544-2
ISSN : 1572-896X
Aparece en las colecciones: DEALI - Artigos publicados em periódicos

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
  Restricted Access
486,02 kBAdobe PDFVisualizar/Abrir

Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.