Título : Caracterização microestrutural de aços baixo carbono por microscopia de força atômica.
Otros títulos : Microstructural characterization of low carbon steels by atomic force microscopy.
Autor : Santos, Tiago Felipe de Abreu
Lopez, Edwar Andrés Torres
Vilela, José Mário Carneiro
Andrade, Margareth Spangler
Cota, André Barros
Palabras clave : Aço carbono microligado com Nb
Microestrutura bainítica
Microscopia de força atômica
Nb-microalloyed low carbon steel
Bainitic microstructures
Fecha de publicación : 2015
Citación : SANTOS, T. F. de A. et al. Caracterização microestrutural de aços baixo carbono por microscopia de força atômica. Revista Latinoamericana de Metalurgia y Materiales, v. 35, p. 118-133, 2015. Disponível em: <http://ve.scielo.org/scielo.php?pid=S0255-69522015000100015&script=sci_abstract&tlng=es>. Acesso em: 07 mar. 2017.
Resumen : A descrição microestrutural de aços é feita frequentemente por meio das técnicas de microscopia óptica e eletrônica de varredura, que permitem identificar as principais fases e constituintes presentes. A complexidade microestrutural dos constituintes formados em maiores taxas de resfriamento, durante o resfriamento contínuo, dificulta a caracterização destes. Em especial, as microestruturas bainíticas e martensíticas fornecem características morfológicas de difícil visualização. A microscopia de força atômica foi usada visando complementar a microscopia óptica e eletrônica de varredura na descrição dos produtos do resfriamento contínuo de um aço baixo carbono com e sem adição de Nb. As amostras foram austenitizadas, algumas temperadas, enquanto outras resfriadas até Ar3 e Ar1 e, então, temperadas. A microscopia de força atômica permitiu determinar que, para ambos os aços, as amostras temperadas, a partir da temperatura de austenitização, apresentaram microestrutura predominantemente martensítica e bainítica. Por outro lado, as amostras interrompidas na Ar3 apresentaram ferrita poligonal e martensita e a formação de ferrita bainítica. Para as amostras temperadas a partir da Ar1, a microestrutura foi essencialmente ferrita e perlita fina.
metadata.dc.description.abstracten: Microstructural characterization of steels is normally performed using optical and scanning electron microscopy which allows identifying the most important phases and constituents in steels. Nevertheless, the microstructural complexity of some constituents during continuous cooling hinders the characterization of them; especially bainitic and martensitic microstructures provide rich morphology characteristics tough to solve properly. In this sense, atomic force microscopy was applied in order to provide complementary information to optical and scanning electronic microscopy in continuous cooling microstructural constituents of a low carbon and a Nb microalloyed low carbon steels. The samples were austenitized, some of them were quenched directly from austenitization temperature and others were cooling to Ar3 and Ar1 temperatures and then quenched. The samples quenched from austenitization temperature showed predominantly bainitic and martensitic microstructures, some microstructural characteristics were only elucidated with the combination between scanning electron microscopy and atomic force microscopy. On the other hand, the samples quenched from Ar3 temperature showed polygonal ferrite and martensite morphologies. Atomic force microscopy has also indicated the occurrence of bainitic ferrite. Concerning samples quenched from Ar1 temperature, the microstructure was essentially ferrite and fine perlite.
URI : http://www.repositorio.ufop.br/handle/123456789/7328
ISSN : 1361-6447
metadata.dc.rights.license: Los autores conservan los derechos de distribuir copias del trabajo publicado para fines docentes o dentro de su institución de afiliación. Fonte: Revista Latinoamericana de Metalurgia y Materiales <http://www.rlmm.org/ojs/index.php/rlmm/about/submissions#copyrightNotice>. Acesso em: 30 out. 2019.
Aparece en las colecciones: DEFIS - Artigos publicados em periódicos

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
ARTIGO_CaracterizaçãoMicroestruturalAços.pdf
  Restricted Access
2,72 MBAdobe PDFVisualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.