http://www.repositorio.ufop.br/jspui/handle/123456789/6769| Título: | Corrosion behavior of UNS S31803 steel with changes in the volume fraction of ferrite and the presence of chromium nitride. |
| Autor(es): | Lacerda, José Carlos de Cândido, Luiz Cláudio Godefroid, Leonardo Barbosa |
| Palavras-chave: | Stainless steel Polarization Pitting corrosion Stress corrosion cracking |
| Data do documento: | 2015 |
| Referência: | LACERDA, J. C. de; CÂNDIDO, L. C.; GODEFROID, L. B. Corrosion behavior of UNS S31803 steel with changes in the volume fraction of ferrite and the presence of chromium nitride. Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing, p. 428-435, 2015. Disponível em: <http://www.sciencedirect.com/science/article/pii/S0921509315304305>. Acesso em: 11 jul. 2016. |
| Resumo: | The goal of this study was to examine the changes caused in stress corrosion cracking and the critical pitting temperature behavior of a UNSS31803 duplex stain less steel due to variations in the ferrite fraction and the presence of chromium nitride in their microstructure. The steel plates were cold rolled and annealed at 1060 °C. Microstructural variations in the plates were produced by thermal annealing treatments a t1200 °C and 1300 °C. Steel annealed at 1060 °C showed greater resistance to stress corrosion cracking than steel annealed at 1300 °C. Steel annealed at 1300 °C had the lowest critical pitting temperature. |
| URI: | http://www.repositorio.ufop.br/handle/123456789/6769 |
| DOI: | https://doi.org/10.1016/j.msea.2015.09.092 |
| ISSN: | 0921-5093 |
| Licença: | O periódico Materials Science and Engineering: A concede permissão para depósito deste artigo no Repositório Institucional da UFOP. Número da licença: 3914191502183. |
| Aparece nas coleções: | DEMET - Artigos publicados em periódicos |
Arquivos associados a este item:
| Arquivo | Descrição | Tamanho | Formato | |
|---|---|---|---|---|
| ARTIGO_CorrosionBehaviorUNS.pdf | 3,03 MB | Adobe PDF | Visualizar/Abrir |
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.