Please use this identifier to cite or link to this item: http://www.repositorio.ufop.br/jspui/handle/123456789/6765
Full metadata record
DC FieldValueLanguage
dc.contributor.authorGodefroid, Leonardo Barbosa-
dc.contributor.authorFaria, Geraldo Lúcio de-
dc.contributor.authorCândido, Luiz Cláudio-
dc.contributor.authorViana, Thiago Gomes-
dc.date.accessioned2016-08-08T18:24:25Z-
dc.date.available2016-08-08T18:24:25Z-
dc.date.issued2015-
dc.identifier.citationGODEFROID, L. B. et al. Failure analysis of recurrent cases of fatigue fracture in flash butt welded rails. Engineering Failure Analysis, v. 55, p. 10.1016, 2015. Disponível em: <http://www.sciencedirect.com/science/article/pii/S135063071500182X>. Acesso em: 11 jul. 2016.pt_BR
dc.identifier.issn1350-6307-
dc.identifier.urihttp://www.repositorio.ufop.br/handle/123456789/6765-
dc.description.abstractMedium carbon steel rails are commonly jointed by flash butt welding procedures. To ensure an adequate service life for the structural component, commonly subjected to fatigue loading, a rigorous quality control should be performed, both in welding parameters and in the surface quality of the welded joint. This work investigated the causes of recurrent failures in railroads, with cracking always initiated in the rail in the region of the welded joint. Two case studies are presented. Aiming to execute the failure analysis, all standard procedures were applied, with a careful assessment of the material characteristics and the fractured surface. It was concluded that, for both cases, fatigue cracks initiated near the weld bead and spread in a brittle mode, leading to premature fracture of the material. An in-depth analysis of the rails showed that the surface finishing of the weld bead was not appropriate, generating undesirable stress concentration. Some undesirable microstructural characteristics were also found in the weld region. A recommendation to control welding parameters and to change the procedure of surface finishing of welded joints was held, aiming to decrease the number of accidents on the railroads.pt_BR
dc.language.isoen_USpt_BR
dc.rightsabertopt_BR
dc.subjectRailspt_BR
dc.subjectFlash butt weldingpt_BR
dc.subjectFatigue crackingpt_BR
dc.titleFailure analysis of recurrent cases of fatigue fracture in flash butt welded rails.pt_BR
dc.typeArtigo publicado em periodicopt_BR
dc.rights.licenseO periódico Engineering Failure Analysis concede permissão para depósito deste artigo no Repositório Institucional da UFOP. Número da licença: 3914191316805.pt_BR
dc.identifier.doihttps://doi.org/10.1016/j.engfailanal.2015.05.022-
Appears in Collections:DEMET - Artigos publicados em periódicos

Files in This Item:
File Description SizeFormat 
ARTIGO_FailureAnalysisRecurrent.pdf3,1 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.