dc.contributor.advisorJunqueira, Rosa Maria Rabelopt_BR
dc.contributor.advisorLins, Vanessa de Freitas Cunhapt_BR
dc.contributor.authorFerreira, Danilo Fontes-
dc.date.accessioned2016-06-02T20:52:44Z-
dc.date.available2016-06-02T20:52:44Z-
dc.date.issued2015-
dc.identifier.citationFERREIRA, Danilo Fontes. Estudo da corrosão de ligas de aço inoxidável e titânio em solução de Ringer. 2015. 100f. Dissertação (Mestrado em Engenharia de Materiais) – Universidade Federal de Ouro Preto, Ouro Preto, 2015.pt_BR
dc.identifier.urihttp://www.repositorio.ufop.br/handle/123456789/6520-
dc.descriptionPrograma de Pós-Graduação em Engenharia de Materiais. Departamento de Engenharia Metalúrgica, Escola de Minas, Universidade Federal de Ouro Preto.pt_BR
dc.description.abstractNeste trabalho foi estudada a resistência à corrosão em solução de Ringer de duas ligas metálicas utilizadas como biomateriais, a liga de titânio ASTM F67Gr1 e o aço inox ASTM F139. Também foi estudado o comportamento da liga de titânio em regime de tribocorrosão em solução de Ringer. A solução de Ringer foi o eletrólito escolhido para a realização desse estudo pelo fato de ser um meio comumente utilizado para simular as condições de corrosão em meio fisiológico. Visando a realização dos testes de tribocorrosão, foi necessário o desenvolvimento de um dispositivo capaz de impor um desgaste mecânico a amostras imersas na solução de Ringer. A resistência à corrosão das ligas foi efetuada através da realização de curvas de polarização potenciodinâmica e evidenciou uma resistência à corrosão muito superior por parte da liga de titânio em relação ao aço inox. Depois de projetado e fabricado o dispositivo gerador de desgaste mecânico, utilizando testes de tribocorrosão em regime potenciostático, foi estudado o comportamento da liga de titânio frente à tribocorrosão. Os testes de tribocorrosão avaliaram as correntes de corrosão, os volumes desgastados, a sinergia entre o desgaste mecânico e corrosivo durante a tribocorrosão e a variação desses parâmetros de acordo com variações na velocidade do penetrador e da carga aplicada sobre ele. Os resultados dos testes de tribocorrosão mostraram a grande influência que a carga e a velocidade do penetrador exercem no desgaste tribocorrosivo, e mostraram também a grande participação do desgaste devido à sinergia, sendo responsável por 32 a 86% do desgaste total nas condições estudadas. ________________________________________________________________________________________pt_BR
dc.description.abstractABSTRACT: In this work, the corrosion resistance in Ringer's solution of two alloys used as biomaterials, ASTM F67Gr1 titanium alloy and stainless steel ASTM F139, was evaluated. The titanium alloy tribocorrosion behavior in Ringer's solution was also studied. The Ringer's solution was the electrolyte chosen in this study because it is a means commonly used to simulate the conditions of corrosion in physiological environment. Aiming at achieving the tribocorrosion tests, the development of a device capable of imposing a mechanical stress on the samples immersed in Ringer's solution was required. The corrosion resistance of the alloys was performed by conducting potentiodynamic polarization curves and results showed a much higher corrosion resistance of the titanium alloy compared to stainless steel. Once designed and manufactured the mechanical wear device, tribocorrosion tests in potentiostatic regime was performed to study the tribocorrosion behavior of the titanium alloy. The tribocorrosion tests evaluated the corrosion currents, the worn volume, the synergy between the mechanical and corrosive degradation during tribocorrosion and the variation of these parameters according to variations in the speed of the indenter and the load applied on it. The results of tribocorrosion tests showed the great influence that the load and indenter speed play in tribocorrosive wear, and also showed the large participation of wear due to synergy, accounting for 32-86% of the total wear in the studied conditions.pt_BR
dc.language.isopt_BRpt_BR
dc.rightsabertopt_BR
dc.subjectAçopt_BR
dc.subjectCorrosãopt_BR
dc.titleEstudo da corrosão de ligas de aço inoxidável e titânio em solução de Ringer.pt_BR
dc.typeDissertacaopt_BR
dc.rights.licenseAutorização concedida ao Repositório Institucional da UFOP pelo autor, 31/05/2016, com as seguintes condições: disponível sob Licença Creative Commons 4.0, que permite copiar, distribuir e transmitir o trabalho, desde que seja citado o autor e licenciante. Não permite o uso para fins comerciais nem a adaptação destapt_BR
dc.contributor.refereeGodoy, Geralda Cristina Durães dept_BR
dc.contributor.refereeManhabosco, Taíse Mattept_BR
Appears in Collections:REDEMAT - Mestrado (Dissertações)

Files in This Item:
File Description SizeFormat 
DISSERTAÇÃO_EstudoCorrosãoLigas.pdf5,85 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons