Title: Suscetibilidade à corrosão sob tensão de um aço UNS S32304 em meios contendo cloretos.
Authors: Barros, Ramon Silveira Assis
metadata.dc.contributor.advisor: Cândido, Luiz Cláudio
Keywords: Corrosão sob tensão
Aço inoxidável
Cloretos
Issue Date: 2015
Citation: BARROS, Ramon Silveira Assis. Suscetibilidade à corrosão sob tensão de um aço UNS S32304 em meios contendo cloretos. 2015. 65f. Dissertação (Mestrado em Engenharia de Materiais) – Universidade Federal de Ouro Preto, Ouro Preto, 2015.
Abstract: Este trabalho foi realizado com o objetivo de se investigar o comportamento do aço inoxidável duplex (AID) UNS S32304 em meios contendo íons cloreto, sob o ponto de vista da corrosão sob tensão (CST). Para tanto, foram realizados ensaios de CST com carga e deformação constantes. Os ensaios de CST com carga constante foram realizados em soluções aquosas com 42% e 35%, em massa, de cloreto de magnésio (MgCl2), em ebulição (143°C e 125°C, respectivamente). O ensaio de CST com deformação constante dos eletrodos foi realizado com solução aquosa contendo 42%, em massa, de MgCl2, também em ebulição (143°C). Foram realizados também ensaios de polarização a fim de se avaliar o comportamento do aço em relação à corrosão por pites. Microscopia óptica e análise química foram feitas para a caracterização do material. Constatou-se a suscetibilidade à CST deste material, quantitativa e qualitativamente, além da influência da concentração de íons cloreto na solução. Essa comparação foi reforçada após a análise microfractográfica dos corpos de prova ensaiados. Os ensaios de polarização potenciostática indicaram que o potencial de pite foi por volta de 400 mVECS em solução aquosa contendo 3,5%, em massa, de cloreto de sódio (NaCl). Por meio de microscopia eletrônica de varredura (MEV) constatou-se a presença de alguns pites formados durante os ensaios de polarização. ________________________________________________________________________________
ABSTRACT : work was carried out in order to investigate the duplex stainless steel UNS S32304 behavior in environments containing chloride ions from the point of view of stress corrosion cracking (SCC). Thus, we performed SCC tests with constant load and constant strain. SCC tests were carried out under constant load in aqueous solutions with 42% and 35% by weight magnesium chloride (MgCl2), boiling (143 ° C and 125 ° C, respectively). The SCC test of constant strain of the electrodes was carried out with an aqueous solution containing 42% by weight MgCl2, also boiling (143 ° C). Were also conducted polarization tests in order to evaluate the steel about pitting corrosion behavior. Optical microscopy and chemical analysis were performed to characterize the material. It was found the susceptibility to SCC of this material, quantitatively and qualitatively, beyond the influence of the concentration of chloride ions in the solution. It was found susceptibility to SCC of this material, quantitatively and qualitatively, beyond the influence of the concentration of chloride ions in the solution. This comparison was reinforced after microfractographic analysis of test specimens. The potentiostatic polarization tests indicated that the pitting potential was around 400 mVSCE in aqueous solution containing 3.5% by weight sodium chloride (NaCl). By means of scanning electron microscopy (SEM) revealed the presence of some pits formed under polarization tests.
Description: Programa de Pós-Graduação em Engenharia de Materiais. Departamento de Engenharia Metalúrgica, Escola de Minas, Universidade Federal de Ouro Preto.
URI: http://www.repositorio.ufop.br/handle/123456789/6398
metadata.dc.rights.license: Autorização concedida ao Repositório Institucional da UFOP pelo autor, 01/03/2016, com as seguintes condições: disponível sob Licença Creative Commons 4.0, que permite copiar, distribuir e transmitir o trabalho, desde que seja citado o autor e licenciante. Não permite o uso para fins comerciais nem a adaptação desta.
Appears in Collections:REDEMAT - Mestrado (Dissertações)

Files in This Item:
File Description SizeFormat 
DISSERTAÇÃO_SuscetibilidadeCorrosãoTensão.pdf3,43 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.