Title: Efeito de impactos repetidos de baixa energia em compósitos pultrudados.
Authors: Morais, Willy Ank de
d'Almeida, José Roberto Moraes
Godefroid, Leonardo Barbosa
Keywords: Compósitos pultrudados
Impacto de baixa energia
Defeitos
Pultruded composites
Low energy impact tests
Issue Date: 2001
Citation: MORAIS, W. A. de; D'ALMEIDA, J. R. M.; GODEFROID, L. B. Efeito de impactos repetidos de baixa energia em compósitos pultrudados. Polímeros, v. 11, p. 27-34, 2001. Disponível em: <http://www.scielo.br/pdf/po/v11n1/v11n1a06.pdf>. Acesso em: 12 nov. 2015.
Abstract: Danos internos podem ser gerados em compósitos de matriz polimérica submetidos a impactos de baixa energia. O efeito repetido de eventos desse tipo pode levar, eventualmente, à falha da estrutura. Neste trabalho dois tipos de perfis pultrudados foram submetidos a impactos por queda livre de peso de 0,5 m e 1,0 m de altura. Os resultados obtidos foram analisados em função da disposição das fibras nos perfis e mostram que a existência de uma camada rica em resina em um dos perfis, contribui para reduzir significativamente o desempenho deste perfil. Este comportamento foi associado à formação prematura de trincas na camada rica em resina. O número de eventos de impacto, o tempo de duração de cada choque e a forma da área danificada foram correlacionados com a presença, ou não, da região rica em resina. Os resultados obtidos indicam ainda que a diferença na microestrutura dos perfis analisados é mais significativa para os ensaios de menor energia (queda de 0,5 m). Para os ensaios de maior energia (queda de 1 m) a configuração do material teve apenas uma importância secundária. ______________________________________________________________________________________________________________
ABSTRACT: Damage can be produced in polymers composite materials submitted to low energy impact events. The cumulative effect of such repetitive impacts could finally cause failure of the structure. In this work two pultruded composites were submitted to drop-weight tests. The results obtained were evaluated according to the fiber distribution in the composites. It was also shown that the presence of a resin rich layer in one of the composites strongly reduces the performance of this composite. This behavior was associated with the development of cracks in the resin rich layer. The number of repeated impacts, the duration of the impact and the shape of the damaged area were correlated to the presence, or the absence, of the resin rich layer. The results obtained also show that the difference between the microstructures of the pultruded profiles analyzed is more significant when low energy impact tests were performed (drop height : 0.5 m). For the tests performed with a higher impact energy (drop height : 1 m) the microstructure plays only a secondary role.
URI: http://www.repositorio.ufop.br/handle/123456789/5879
ISSN: 16785169
metadata.dc.rights.license: Todo o conteúdo do periódico Polímeros, exceto onde identificado, está licenciado sob uma licença Creative Commons que permite copiar, distribuir e transmitir o trabalho em qualquer suporte ou formato desde que sejam citados o autor e o licenciante. Fonte: <http://www.scielo.br/scielo.php?script=sci_serial&pid=0104-1428&nrm=iso&rep=&lng=pt>. Acesso em: 05 nov. 2015.
Appears in Collections:DEMET - Artigos publicados em periódicos

Files in This Item:
File Description SizeFormat 
ARTIGO_EfeitoImpactosRepetidos.pdf150,87 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.