Title: Tenacidade à fratura e crescimento de trinca por fadiga de dois aços bifásicos de emprego automotivo.
Authors: Godefroid, Leonardo Barbosa
Cândido, Luiz Cláudio
Cangue, Feliciano
Rodrigues, Elenice Maria
Gritti, João Alfredo
Melo, Túlio Magno Füzessy de
Keywords: Tenacidade à fratura
Fatigue resistance
Aços bifásicos
Automotive application
Issue Date: 2005
Citation: GODEFROID, L. B. et al. Tenacidade à fratura e crescimento de trinca por fadiga de dois aços bifásicos de emprego automotivo. Revista Escola de Minas, Ouro Preto, v. 58, n. 1, p. 45-50, 2005. Disponível em: <http://www.scielo.br/scielo.php?pid=S0370-44672005000100008&script=sci_arttext>. Acesso em: 09 abr. 2015.
Abstract: O presente trabalho avaliou a tenacidade à fratura e a resistência à propagação de trinca de fadiga de dois aços bifásicos, um deles com teor significativo de cromo e o outro com teor significativo de silício. Com relação à tenacidade, observou-se uma ligeira superioridade (maiores valores) do aço ao silício em relação ao aço ao cromo. Verificou-se, também, o efeito deletério do aumento da profundidade do entalhe lateral dos corpos-de-prova sobre a tenacidade. Não foi encontrado efeito significativo de anisotropia. Com relação à fadiga, os resultados mostraram que os dois aços apresentam um comportamento semelhante com inexistência de anisotropia. A elevação na razão R entre tensões provocou um aumento na taxa de propagação de trinca e um decréscimo no valor de deltaKth dos materiais.
metadata.dc.description.abstracten: Fracture toughness JQ and fatigue crack growth da/dN x deltaK have been studied in two dual-phase steels used in the automotive industry, with 8.8% to 12.5% of martensite volumetric fraction. The main difference between the steels is the chemical composition: one of the steels had chromium additions while the other had silicon as an alloy element. Silicon steel presents higher fracture toughness than chromium steel. It was not noticed significant effect of anisotropy in both steels, while an increase of side grooves decreased the value of JQ of the materials. The two steels present a similar behavior in fatigue crack growth resistance with no significant effect of anisotropy. An increase of R ratio increased the crack growth rates and decreased the value of deltaKth of the materials.
URI: http://www.repositorio.ufop.br/handle/123456789/5494
metadata.dc.identifier.doi: http://dx.doi.org/10.1590/S0370-44672005000100008
ISSN: 1807-0360
metadata.dc.rights.license: A Revista Escola de Minas - REM - autoriza o depósito de cópia de artigos dos professores e alunos da UFOP no Repositório Institucional da UFOP. Contato em 12 set. 2013.
Appears in Collections:DEMET - Artigos publicados em periódicos

Files in This Item:
File Description SizeFormat 
ARTIGO_TenacidadeFraturaCrescimento.pdf415,16 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.