Título : Effect of volume fraction of phases and precipitates on the mechanical behavior of UNS S31803 duplex stainless steel.
Autor : Lacerda, José Carlos de
Cândido, Luiz Cláudio
Godefroid, Leonardo Barbosa
Palabras clave : Duplex stainless steel
Microstructure
Tensile and fatigue tests
Fecha de publicación : 2015
Citación : LACERDA, J. C. de; CÂNDIDO, L. C.; GODEFROID, L. B. Effect of volume fraction of phases and precipitates on the mechanical behavior of UNS S31803 duplex stainless steel. International Journal of Fatigue, v. 74, p. 38, 2015. Disponível em: <http://www.sciencedirect.com/science/article/pii/S0142112314003260>. Acesso em: 09 abr. 2015.
Resumen : Mechanical properties of a grade UNS S31803 duplex stainless steel were studied. Samples were annealed at three different temperatures, 1060 C, 1200 C, and 1300 C, to change the a/c proportion, to precipitate undesirable phases (for example, a0 , r and chromium nitrides), and to study the effect of the microstructure on the mechanical behavior. Specimens with a thickness of 1.8 mm were prepared according to ASTM standards and tested at room temperature. Tensile tests were conducted using displacement control at a rate of 5 mm/min. Force-controlled constant amplitude axial fatigue tests were conducted at a frequency of 30 Hz and an R stress ratio of 0.1. Microstructural analyses, performed by optical microscopy and scanning electron microscopy, showed the following modifications to the microstructure: changes in the phase volume fractions, the phase grain growths, and the morphology of the c-phase and the precipitation of chromium nitrides in the a-phase. The mechanical properties of the steel were significantly changed due to the changed microstructure. The results demonstrate the sensitivity of the steel to the annealing temperature.
URI : http://www.repositorio.ufop.br/handle/123456789/5347
metadata.dc.identifier.doi: https://doi.org/10.1016/j.ijfatigue.2014.12.015
ISSN : 0142-1123
metadata.dc.rights.license: O periódico International Journal of Fatigue concede permissão para depósito deste artigo no Repositório Institucional da UFOP. Número da licença: 3624211041567.
Aparece en las colecciones: DEMET - Artigos publicados em periódicos

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
ARTIGO_EffectVolumeFraction.pdf3,28 MBAdobe PDFVisualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.