dc.identifier.citationSIQUEIRA, K. P. F. et al. Structural and thermal evolution studies of LaSbO4 ceramics prepared by solid-state reaction method. Materials Chemistry and Physics, v. 140, p. 255-259, 2013. Disponível em: <>. Acesso em: 02 fev. 2015.pt_BR
dc.description.abstractThis work investigates the thermal evolution of LaSbO4 ceramics produced by solid-state method in the temperature range 700e1500 _C, for 6 h. Besides the expected phase transitions, a thermal decomposition at high temperatures to La3SbO7 was observed and discussed. The results showed that the phase LaSbO4 can be obtained only below 1450 _C, while temperatures lower than 1100 _C are not able to produce crystalline structures. The samples were submitted to X-ray diffraction and Raman scattering measurements aiming to determine their crystal structures. LaSbO4 materials exhibited monoclinic structures, space group P21/m ¼ C2 2h(#11), with Z ¼ 4. It was verified that all the 36 Raman-active modes predicted by group-theory calculations were observed. Also, the symmetries could be discerned by using polarized Raman scattering, which allow us to assign the gerade modes. Luminescence properties of LaSbO4 were investigated and the results showed that this compound exhibits sensitivity of the host lattice to UV excitation. PL spectra excited at 360 nm have a blue emission band maximum at 428 nm, corresponding to the self-activated luminescence center of LaSbO4.pt_BR
dc.subjectElectronic materialspt_BR
dc.subjectRaman spectroscopy and scatteringpt_BR
dc.subjectCrystal structurept_BR
dc.titleStructural and thermal evolution studies of LaSbO4 ceramics prepared by solid-state reaction method.pt_BR
dc.typeArtigo publicado em periodicopt_BR
dc.rights.licenseO periódico Materials Chemistry and Physics concede permissão para depósito deste artigo no Repositório Institucional da UFOP. Número da licença: 3577130509795.pt_BR
Appears in Collections:DEQUI - Artigos publicados em periódicos

Files in This Item:
File Description SizeFormat 
ARTIGO_StructuralThermalEvolution.pdf486,19 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.