Title: Influência de cátions Ca2+, Mg2+ e Mn2+ na flotação reversa de minério de ferro.
Authors: Lelis, Deisiane Ferreira
metadata.dc.contributor.advisor: Lima, Rosa Malena Fernandes
Keywords: Minérios de ferro
Flotação
Issue Date: 2014
Citation: LELIS, D. F. Influência de cátions Ca2+, Mg2+ e Mn2+ na flotação reversa de minério de ferro. 2014. 88 f. Dissertação (Mestrado em Engenharia Mineral) - Universidade Federal de Ouro Preto, Ouro Preto, 2014.
Abstract: Este trabalho teve por objetivo investigar a influência dos cátions Ca2+, Mg2+ e Mn2+ na flotação catiônica de minério de ferro e a possibilidade do uso de complexante desses íons metálicos para uma maior seletividade no processo. Em uma primeira fase foram efetuados ensaios de microflotação dos minerais quartzo e hematita, usando acetato de eteramina com 50% de grau de neutralização (Flotigam EDA) em pH 10,5 nas dosagens de 2,5 e 50 mg/L que foram as concentrações de máxima flotabilidade para o quartzo (95,5%) e hematita (96,5%), respectivamente. Observou-se que nessas condições o amido de milho era pouco eficiente na depressão do quartzo. O inverso foi observado para a hematita, onde a dosagem de 10 mg/L foi capaz de quase anular a flotabilidade da mesma. Com a adição de CaCl2, MgCl2 e MnCl2, observou-se a depressão tanto do quartzo quanto da hematita para todas as dosagens testadas, sendo a máxima depressão na concentração de 200 mg/L. O uso do complexante sal dissódico de ácido etilenodiaminotetracético (EDTA) mostrou-se eficiente em altas concentrações (400 mg/L para CaCl2, 600 e 700 mg/L para MnCl2 e MgCl2, respectivamente) para ambos minerais. De modo geral, houve diminuição do módulo dos valores de potencial zeta negativo em pH 10,5 dos minerais (quartzo e hematita) em relação aos valores de potencial zeta dos mesmos na ausência dos sais estudados e da combinação dos reagentes (sais/amido, sais/EDTA/amido e sais/ EDTA/ amido/ amina). Verificou-se nos espectros infravermelhos dos minerais (hematita e quartzo) usados nos ensaios de adsorção a presença comprovada do hidróxido Mg(OH)2 sobre a superfície de ambos minerais. No caso dos ensaios efetuados com MnCl2, verificou-se a precipitação do próprio sal sobre a superfície dos minerais. Logo, pode-se afirmar que há adsorção dos cátions por atração eletrostática dos mesmos com as superfícies dos minerais carregados negativamente (potencial zeta) e precipitação do hidróxido Mg(OH)2 presentes na solução (espectros infravermelhos).
metadata.dc.description.abstracten: This study aimed to investigate the influence of cations Ca2+, Mg2+ and Mn2+ on the cationic flotation of iron ore and the possibility of complexing these metallic ions to improve the process selectivity. In a first stage microflotation trials were performed with the minerals quartz and hematite using etheramine acetate at 50% degree of neutralization (Flotigam EDA) at pH 10.5 in concentrations of 2.5 and 50 mg/L at the maximum floatability levels were achieved for quartz (95.5%) and hematite (96.5%), respectively. It was observed that under these conditions corn starch was ineffective as quartz depressant. On the other hand, the dosage of 10 mg/L was able to almost cancel the floatability of hematite. With the addition of CaCl2, MgCl2 and MnCl2 it was observed depression of quartz as well as of hematite for all tested concentrations with a maximum depression achieved at a concentration of 200 mg/L. The use of the complexing agent disodium salt of ethylenediamine tetraacetic acid (EDTA) was effective at high concentrations (400 mg/L for CaCl2, 600 and 700 mg/L for MnCl2 and MgCl2, respectively) for both minerals. Overall, there was a decrease of the modulus of the negative zeta potential values at pH 10.5 of the minerals (quartz and hematite) with respect to the zeta potential values in the absence of the studied salts and combination of reagents (salts/starch, salts/EDTA/salts and starch/EDTA/starch/amine). It was observed in the infrared spectra the presence of Mg(OH)2 on the surface of both minerals. In the case of experiments carried out with MnCl2, there was precipitation of the salt itself on the surface thereof. Therefore, it can be stated that there is adsorption of cations by electrostatic onto the surfaces of negatively charged minerals (zeta potential) and precipitation of the hydroxide Mg(OH)2 present in solution (infrared spectra).
Description: Programa de Pós-Graduação em Engenharia Mineral. Departamento de Engenharia de Minas, Escola de Minas, Universidade Federal de Ouro Preto.
URI: http://www.repositorio.ufop.br/handle/123456789/3609
metadata.dc.rights.license: Autorização concedida ao Repositório Institucional da UFOP pelo autor(a), 26/08/2014, com as seguintes condições: disponível sob Licença Creative Commons 3.0, que permite copiar, distribuir e transmitir o trabalho, desde que seja citado o autor e licenciante. Não permite o uso para fins comerciais nem a adaptação desta.
Appears in Collections:PPGEM - Mestrado (Dissertações)

Files in This Item:
File Description SizeFormat 
DISSERTAÇÃO_InfluênciaCationFlotação.pdf2,31 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons