Title: Comportamento em fadiga de um aço inoxidável duplex UNS S31803 envelhecido termicamente.
Authors: Costa, Junia Maria Gândara
metadata.dc.contributor.advisor: Cândido, Luiz Cláudio
Godefroid, Leonardo Barbosa
Lacerda, José Carlos de
Keywords: Fadiga
Aço inoxidável - duplex
Fase sigma
Fase alfa linha
Issue Date: 2019
metadata.dc.contributor.referee: Godefroid, Leonardo Barbosa
Castro, Geovane Martins de
Teixeira, Ricardo Luiz Perez
Lacerda, José Carlos de
Cândido, Luiz Cláudio
Citation: COSTA, Junia Maria Gândara. Comportamento em fadiga de um aço inoxidável duplex UNS S31803 envelhecido termicamente. 2019. 81 f. Dissertação (Mestrado em Engenharia de Materiais) – Escola de Minas, Universidade Federal de Ouro Preto, Ouro Preto, 2019.
Abstract: Os aços inoxidáveis duplex UNS S31803 apresentam resistência mecânica elevada com alta resistência à corrosão, isto se deve a sua microestrutura composta pelas fases ferrita e austenita em igual proporção, que contribui para resistência à corrosão intergranular. Quando submetido a tratamentos isotérmicos em certas faixas de temperatura, pode ocorrer precipitação de nitretos, carbonetos e fases terciárias, tais como: fase sigma e fase alfa linha. Essas fases alteram as propriedades mecânicas e são deletérias a resistência à corrosão. Os efeitos das fases nas propriedades mecânicas foram analisados. Para a precipitação das fases foram realizados tratamentos isotérmicos a 500ºC por 144 horas (fase alfa linha) e a 850ºC por 80 minutos (fase sigma). Os resultados dos efeitos das fases relatadas foram obtidos a partir de análise microestrutural e os seguintes ensaios mecânicos: tração, dureza e fadiga (σa x Nf). Constatou-se a presença de fase sigma nos contornos de grão, o aumento da resistência mecânica com perda de tenacidade, o aumento na dureza e na resistência à fadiga. Quanto à fase alfa linha, também houve aumento da resistência mecânica com menor perda de ductilidade comparado com a fase sigma. No que diz respeito ao comportamento em fadiga do material tratado a 500ºC, pôde-se inferir que na região de alto ciclo o material apresentou melhor desempenho, porém na vida infinita não houve alteração significativa comparado ao material sem tratamento.
metadata.dc.description.abstracten: Duplex stainless steels UNS S31803 exhibit high mechanical strength with high corrosion properties, due to its microstructure composed by the phases ferrite and austenite, in equal proportion, which contributes to intergranular corrosion resistance. When the material is submitted to isotherms in certain temperature ranges, some precipitations are able to occur, as nitrites, carbides and third phases may occur, such as: sigma phase and alpha line. These phases modify the mechanical properties and are deleterious to corrosion resistance. The effects of the phases on the mechanical properties were analyzed. To precipitate these third phases, isothermals treatments were done, at 500°C for 144 hours (alpha prime) and at 850ºC for 80 minutes (sigma phase). The results of the effects were obtained from the microstructural analysis and the following mechanical tests: traction, hardness and fatigue (σa x Nf). It was verified the presence of a sigma phase in the grain boundary, an increased on the mechanical resistance with loss of tenacity, increase in the hardness and increase in the fatigue resistance. There were an increase in mechanical resistance with the precipitation of alpha prime, although less loss of ductility than sigma phase. Regarding the fatigue behavior of the material heat treated at 500ºC, it can be concluded that in the region of high cycle, the material presented better performance, however, the infinity life was no affected by the material without treatment.
Description: Programa de Pós-Graduação em Engenharia de Materiais. Departamento de Engenharia Metalúrgica, Escola de Minas, Universidade Federal de Ouro Preto.
URI: http://www.repositorio.ufop.br/handle/123456789/11708
metadata.dc.rights.license: Autorização concedida ao Repositório Institucional da UFOP pelo(a) autor(a) em 16/08/2019 com as seguintes condições: disponível sob Licença Creative Commons 4.0 que permite copiar, distribuir e transmitir o trabalho desde que sejam citados o autor e o licenciante.
Appears in Collections:REDEMAT - Mestrado (Dissertações)

Files in This Item:
File Description SizeFormat 
DISSERTAÇÃO_ComportamentoFadigaAço.pdf4,97 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons