dc.identifier.citationCARDOSO, A. F. de M. et al. Secondary recrystallization characteristics of 3%Si grain-oriented electrical steel. Journal of Materials Research and Technology - JMR&T, v. 8, n. 1, p. 240-245, jan./mar. 2018. Disponível em: <>. Acesso em: 19 mar. 2019.pt_BR
dc.description.abstractA secondary recrystallization Lab study focusing on the secondary recrystallization temper- ature and magnetic properties was carried out on cold rolling industrial samples of 3%Si grain-oriented electrical steel produced by low slab reheating temperature technology. The results showed a secondary recrystallization temperature, determined by the observed grain size change, of 1080 ◦C with annealing interruption and of 1060 ◦C in annealing for 50 h at constant temperature. In addition, the best set of magnetic properties, the higher induction and the lower core loss values, was achieved by annealing the samples during 50 h at 1070 ◦C constant temperature.pt_BR
dc.subjectGrain-oriented steelpt_BR
dc.subjectMagnetic propertiespt_BR
dc.titleSecondary recrystallization characteristics of 3%Si grain-oriented electrical steel.pt_BR
dc.typeArtigo publicado em periodicopt_BR
dc.rights.licenseThis is an open access article under the CC BY-NC-ND license ( Fonte: o próprio artigo.pt_BR
Appears in Collections:DEFIS - Artigos publicados em periódicos

Files in This Item:
File Description SizeFormat 
ARTIGO_SecondaryRecrystallizationCharacteristics.pdf1,31 MBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.