Title: Simultaneous decarburizing and nitriding : effects on structure and magnetic properties of 3%Si grain-oriented electrical steel.
Authors: Vilela, Tony Jefferson Sales
Fonseca, Ângelo José de Faria
Paolinelli, Sebastião da Costa
Cota, André Barros
Keywords: Electrical steels
Issue Date: 2018
Citation: VILELA, T. J. S. et al. Simultaneous decarburizing and nitriding : effects on structure and magnetic properties of 3%Si grain-oriented electrical steel. REM - International Engineering Journal, Ouro Preto, v. 71, n. 4, p. 599-604, out./dez. 2018. Disponível em: <http://www.scielo.br/scielo.php?script=sci_abstract&pid=S2448-167X2018000400599&lng=en&nrm=iso>.
Abstract: Lab experiments were carried out to check the effect of some process parameters of nitriding, performed simultaneously with decarburization, on magnetic properties of 3%Si Grain-oriented silicon steel produced by a low slab reheating technology. The samples of (GO) 3% Si steel collected as 0.27mm cold-rolled were submitted to a continuous annealing process at two temperatures, 860 and 900°C; three annealing times, 63.6, 95.4, and 119.25s; and three ammonia flows 0.1, 0.2, and 0.4Nm3/h. The nitrogen content obtained after the treatments was much higher than those obtained by the currently used process, and it increased as the ammonia flow rates and soaking times were increased, hindering the primary grain growth that adversely affected the magnetic properties. The increase of annealing temperature improved the decarburization and the magnetic properties. The best magnetic properties were found in the sample with the highest primary grain size and the lowest amount of absorbed nitrogen. The success of this practice, in terms of magnetic properties, was pointed out to be based on a drastic reduction on strip nitrogen increase.
URI: http://www.repositorio.ufop.br/handle/123456789/11467
metadata.dc.identifier.doi: http://dx.doi.org/10.1590/0370-44672017710076
ISSN: 1807-0353
metadata.dc.rights.license: A REM - International Engineering Journal - autoriza o depósito de cópia de artigos dos professores e alunos da UFOP no Repositório Institucional da UFOP. Licença concedida mediante preenchimento de formulário online em 12 set. 2013.
Appears in Collections:DEFIS - Artigos publicados em periódicos

Files in This Item:
File Description SizeFormat 
ARTIGO_SimultaneousDecarburizingNtriding.pdf1,89 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.