Title: Síntese e caracterização de mulita utilizando sílica obtida da casca de arroz.
Other Titles: Synthesis and characterization of mullite using silica from rice husk.
Authors: Gonçalves, Gislayne Elisana
Sabioni, Antônio Claret Soares
Ferraz, Wilmar Barbosa
Costa, Geraldo Magela da
Brito, Walter de
Dias, José Alves
Garcia, Fillipe Augusto da Costa
Issue Date: 2009
Citation: GONÇALVES, G. E. et al. Síntese e caracterização de mulita utilizando sílica obtida da casca de arroz. Rem: Revista Escola de Minas, v. 62, n. 3, p. 367-372, jul./set. 2009. Disponível em: <http://www.scielo.br/pdf/rem/v62n3/v62n3a16.pdf>. Acesso em: 13 jul. 2012.
Abstract: Mulita com composição 1,4 Al2O3.SiO2 foi sintetizada a partir de α-alumina comercial (Alfa Cesar Company) e de sílica obtida da calcinação da casca de arroz. Essa sílica possui alta área superficial, alta pureza e pequeno diâmetro médio de partícula. Pós de sílica e de alumina foram misturados na proporção estequiométrica 3Al2O3-2SiO2 correspondente a 71,8 % em peso de Al2O3 e 26,2 % em peso de SiO2, homogeneizados em moinho de disco orbital de alumina antes e após a calcinação a 1100ºC, durante 4 h, ao ar. Em seguida, os pós foram prensados uniaxialmente sob uma pressão de 1200 MPa. Os corpos verdes foram sinterizados a 1650ºC, por 4 h, ao ar. As densidades dos corpos sinterizados foram determinadas pelo método hidrostático. As caracterizações química e estrutural foram realizadas por ICP, DRX e MAS RMN de 29Si, respectivamente, e a análise microestrutural por MEV. Os resultados obtidos mostram que é possível sintetizar cerâmica mulita de alta pureza, com pouca fase vítrea, a partir da α-alumina e sílica, obtida da casca de arroz purificada e calcinada.
metadata.dc.description.abstracten: Mullite, composed of 1,4Al2O3.SiO2 was synthesized using commercial α- alumina (Alpha Cesar Company) and silica obtained from the calcinations of rice husk. This silica exhibits a high specific surface area, high purity and small average particle diameter. Silica (26.2 wt.%) and α-alumina powders (71.8 wt.%) were mixed and homogenized using an alumina orbital disc mill before and after the calcinations at 1100ºC for 4 h in an air atmosphere. Then, the powders were pressed uniaxially at a pressure of 1200 MPa. The green compacts were sintered at 1650ºC, for 4 h, in air. The density of compacted sintering samples was determined using the hydrostatic method. The chemical and structural properties were observed using ICP (Inductively Coupled Plasma), XRD (X-ray diffraction) and 29Si MAS (Magic Angle Spinning) NMR (Nuclear Magnetic Resonance) and the microstructural characterization performed using SEM (Scanning Electron Micrography). The results show that it is possible to synthesize mullite ceramic of high-purity and with little glassy phase from the α-alumina and silica obtained from the rice husk that is purified and calcinated.
URI: http://www.repositorio.ufop.br/handle/123456789/1112
ISSN: 03704467
metadata.dc.rights.license: A REM - Revista Escola de Minas - autoriza o depósito de cópia de artigos dos professores e alunos da UFOP no Repositório Institucional da UFOP. Licença concedida mediante preenchimento de formulário online em: 12 set. 2013.
Appears in Collections:DEFIS - Artigos publicados em periódicos

Files in This Item:
File Description SizeFormat 
ARTIGO_SínteseCaracterizaçãoMulita.pdf672,95 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.