Title: Influência da configuração da SEN no comportamento fluidodinâmico em molde de Beam Blank.
Other Titles: Influence of SEN configuration in Beam Blank cast fluidodynamic behavior.
Authors: Gabriel, Weslei Viana
Peixoto, Johne Jesus Mol
Alves, Gesiane Letícia
Silva, Carlos Antônio da
Silva, Itavahn Alves da
Seshadri, Varadarajan
Keywords: Lingotamento contínuo
Válvula submersa
Fluxo de fluido
Continuous casting
Fluid flow
Issue Date: 2017
Citation: GABRIEL, W. V. et al. Influência da configuração da SEN no comportamento fluidodinâmico em molde de Beam Blank. Tecnologia em metalurgia, materiais e mineração, São Paulo, v. 15, p. 226-231, jul./set. 2018. Disponível em: <http://www.tecnologiammm.com.br/doi/10.4322/2176-1523.1601>. Acesso em: 13 fev. 2019.
Abstract: Utilizando técnicas de modelagem física e matemática comparou-se o fluxo de fluido no interior do molde de beam blank alimentado por apenas uma válvula submersa, com 3 e 4 portas na saída respectivamente. Na válvula com 4 portas, observou-se que para um diâmetro da porta de saída inferior de 10mm não houve alterações significativas no comportamento do fluxo, comparado à válvula com apenas três portas laterais. Ao aumentar o diâmetro para 16mm, houve alteração significativa do perfil de velocidade, reduzindo a assimetria de fluxo, fato que pode contribuir para a redução no gradiente térmico ao longo do molde, diminuindo a possibilidade de ocorrência de defeitos no material lingotado. Com o aumento da dimensão da porta inferior observou-se também redução na velocidade de impacto do jato principal e consequentemente reduziu-se a velocidade do fluxo ascendente, o que evita refusão da pele e entranhamento de escória.
metadata.dc.description.abstracten: Physical and mathematical simulations was used to characterize the fluid flow inside a beam blank mold fed with one submerged entry nozzles containing three and four ports respectively. Comparing both systems was observed that when this fourth port had diameter equal 10mm no significantly changes could be seen in relation to the SEN without this port. Increasing the diameter to 16mm change the velocity profile significantly, reducing the asymmetry of the flow decreasing the thermal gradient in the mold and consequently the possibility of defects occurrence on the product. Was observed too the reduction of impingement velocity with the higher diameter of the base port. This reduce the velocity of the ascendant flow, avoiding remelting of the skin and slag entrainment.Physical and mathematical simulations was used to characterize the fluid flow inside a beam blank mold fed with one submerged entry nozzles containing three and four ports respectively. Comparing both systems was observed that when this fourth port had diameter equal 10mm no significantly changes could be seen in relation to the SEN without this port. Increasing the diameter to 16mm change the velocity profile significantly, reducing the asymmetry of the flow decreasing the thermal gradient in the mold and consequently the possibility of defects occurrence on the product. Was observed too the reduction of impingement velocity with the higher diameter of the base port. This reduce the velocity of the ascendant flow, avoiding remelting of the skin and slag entrainment.
URI: http://www.repositorio.ufop.br/handle/123456789/10818
ISSN: 21761523
metadata.dc.rights.license: Este é um artigo de acesso aberto distribuído sob os termos da licença Creative Commons CC BY-NC-ND (Attribution-NonCommercial-NoDerivs) - https:// creativecommons.org/licenses/by-nc-nd/4.0/. Fonte: o próprio artigo
Appears in Collections:DEMET - Artigos publicados em periódicos

Files in This Item:
File Description SizeFormat 
ARTIGO_InfluenceConfiguraçãoSen.pdf1,33 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.