Title: Efeito dos tratamentos térmicos de têmpera e particionamento na microestrutura e propriedades mecânicas de aços API aplicados em indústrias de óleo e gás.
Authors: Silva, Amanda de Paiva
metadata.dc.contributor.advisor: Cândido, Luiz Cláudio
Trindade, Vicente Braz
Keywords: Têmpera e particionamento
API 5L
API 5CT
Microestrutura e propriedades mecânicas
Soldagem
Issue Date: 2018
metadata.dc.contributor.referee: Cândido, Luiz Cláudio
Trindade, Vicente Braz
Lima, Margarida Márcia Fernandes
Queiroz, Rhelman Rossano Urzedo
Citation: SILVA, Amanda de Paiva. Efeito dos tratamentos térmicos de têmpera e particionamento na microestrutura e propriedades mecânicas de aços API aplicados em indústrias de óleo e gás. 2018. 104 f. Dissertação (Mestrado em Engenharia de Materiais) – Escola de Minas, Universidade Federal de Ouro Preto, Ouro Preto, 2018.
Abstract: A exploração da maioria das reservas de petróleo, atualmente, é submarina, dita offshore, e devido à crescente profundidade das mesmas, é necessário que a perfuração de poços e o transporte do petróleo e gás seja feito de forma, a minimizar o risco de acidentes. Dessa forma, buscando-se atender as exigências dos aços empregados nas indústrias petrolíferas, podem ser empregadas rotas não tradicionais de tratamentos térmicos. Neste trabalho, foram estudados três aços que atendem à Norma API 5L (2013) ou API 5CT (2011). Foram empregados tratamentos térmicos, denominados têmpera e particionamento (Q&P). Os efeitos destes na microestrutura foram avaliados e relacionados às alterações nas propriedades mecânicas dos aços analisados. As amostras foram analisadas por microscopia óptica e microscopia eletrônica de varredura (MEV), a fim de identificar as fases e constituintes. As propriedades mecânicas foram avaliadas empregando-se ensaios de tração, microdureza Vickers e impacto Charpy. Além disso, submeteram-se esses materiais, a procedimento de soldagem pelo processo GTAW (TIG), após o referido tratamento térmico. Os resultados foram então, comparados aos obtidos quando se emprega o tratamento térmico de têmpera e revenimento (Q&T) nos mesmos aços. Pode-se perceber a presença de austenita retida na microestrutura final do material, após estes tratamentos térmicos, que concede aumento de dureza ao material, sem comprometer a ductilidade.
metadata.dc.description.abstracten: The recent explorations of oil and gas are manly underwater, offshore, and due to the increase of the depth, is necessary that the drilling and the transport of these products are made to prevent accidents. The demands of the oil industries in regard of steels, is increasing to guarantee the safety even in extreme conditions, besides the reduction of the costs of these companies. Three types of seamless steels were analyzed in this project. Two of them follow the Norm API 5L and one, API 5CT. It was used a non-tradition rout of thermic treatments called quenching and partitioning (Q&P). It consists of a rapid cooling from the austenitized temperature, however, avoiding the martensitic transformation in all the material. Then, they are reheated to temperatures such as 400°C; 450°C; 500°C e 600°C. The samples were kept in these temperatures, so the partitioning could happen, and were quickly cooled to room temperature. The effects of the quenching and partitioning treatment in the microstrucute will be evaluated regarding the influences into the mechanical properties of these steels. The objectives of this treatment are to obtain retained austenite, which grants hardness without affecting the ductility of the material. The samples were analyzed to identify the microstructure, using optic microscopy and scanning electron microscopy (S.E.M.). The mechanical properties were studied using tensile tests, Vickers microhardness e Charpy impact. Furthermore, the samples were submitted to GTAW welding procedure, after this thermic treatment. The results were compared with the quenching and tempering treatment (Q&T) in the same steels.
Description: Programa de Pós-Graduação em Engenharia de Materiais. Departamento de Engenharia Metalúrgica, Escola de Minas, Universidade Federal de Ouro Preto.
URI: http://www.repositorio.ufop.br/handle/123456789/10623
metadata.dc.rights.license: Autorização concedida ao Repositório Institucional da UFOP pelo(a) autor(a) em 08/01/2019 com as seguintes condições: disponível sob Licença Creative Commons 4.0 que permite copiar, distribuir e transmitir o trabalho desde que sejam citados o autor e o licenciante. Não permite a adaptação.
Appears in Collections:REDEMAT - Mestrado (Dissertações)

Files in This Item:
File Description SizeFormat 
DISSERTAÇÃO_EfeitoTratamentosTérmicos.pdf5,8 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons