Title: Kinetics of magnetic ageing of 2%Si non-oriented grain electrical steel.
Authors: Oliveira Júnior, José Rogério de
Monteiro, Renata Aparecida
Paolinelli, Sebastião da Costa
Cota, André Barros
Keywords: Magnetic ageing index
Vickers hardness
Issue Date: 2018
Citation: OLIVEIRA JÚNIOR, J. R. de et al. Kinetics of magnetic ageing of 2%Si non-oriented grain electrical steel. Materials Research, v. 21, n.1, p. e20170575, out. 2018. Disponível em: <>. Acesso em: 16 jun. 2018.
Abstract: The effect of carbon content on the magnetic ageing index and Vickers hardness evolution on annealed samples of 2%Si non-oriented grain electrical steel was studied. Samples with 40 and 60ppm carbon content were subjected at ageing temperatures of 200 and 225ºC, respectively. During the ageing treatment, the cycle was interrupted on several time intervals in order to obtain the core loss and to determine Vickers hardness. The precipitates were characterized using scanning electron microscope (SEM). Using the software MatCalc, computer simulations of ε-carbide precipitation were performed and compared with experimental data from literature. The results for both carbon contents showed that the maximum hardness value was achieved in shorter time than that to achieve the maximum magnetic ageing, indicating that the critical size of precipitates more harmful to the magnetic properties is larger than the ones that maximize the hardness.
ISSN: 15161439
metadata.dc.rights.license: O periódico Materials Research dá permissão ao RI/UFOP para depositar uma cópia eletrônica dos artigos publicados por esse periódico em que ao menos um dos autores é aluno ou professor da UFOP. Contato via email em 25 out. 2013.
Appears in Collections:DEFIS - Artigos publicados em periódicos

Files in This Item:
File Description SizeFormat 
ARTIGO_KineticsMagneticAgeing.pdf1,71 MBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.